Changes in the amount of adhesion of Streptococcus mutans to pit and fissure sealant incorporating cerium oxide nano particles(CNPs)

Seong-Sook Lee1   Young-Min Park1   Dong-Ae Kim1,*   

Department of Dental Hygiene, Yeoju Institute of Technology

Abstract

Objectives: The aim of this study was to investigated the surface roughness and change in the amount of adhesion of Streptococcus mutans to the commercial pit and fissure sealant containing cerium oxide nano particles(CNPs). Methods: The CNPs was incorporated into a commercial pit and fissure sealant at 0-4.0 wt%. Disk Specimens (φ 10 mm × 2 mm) were prepared by light polymerization the front and back for 40s. Average surface roughness was measured and Streptococcus mutans adhesion was observed under confocal laser scanning microscopy (CLSM) after 24 hour. Data were statistically analyzed by one-way ANOVA and Tukey HSDa post-hoc test. Results: Difference of the surface roughness(Ra) between groups was not statistically significant in both non CNPs group and CNPs group(p>0.05). In CNPs group, the amount of S. mutans adhesion was significantly different between control group and decreased in order of CNPs 4.0, CNPs 0.5, CNPs 1.0 and CNPs 2.0(p<0.05). Conclusions: Within the limitation of this study, these aspects of oral bacteria performances suggest potential usefulness of the CNPs incorporation, especially CNPs 1% and 2%, in pit and fissure sealant for inducing antibacterial effect.

Figures & Tables

Fig. 1. The surface roughness(Ra) values of experimental groups (n=5)